UBE UBE Hybrid Polycarbonate Diol PH Series PH-50 PH-100 PH-200 PH-300

                                                                

Product Introduction
“ETERNACOLL® PH” is the brand name of a hybrid polycarbonate diol developed by Ube Kosan. This polycarbonate diol uses 1,5-pentanediol and 1 ,6-Hexanediol is a polymerized monomer.

Specifications

Product indicators

PH 50

PH 100

PH 200

PH 300

Appearance

Viscous liquid

Average molecular weight

Ca. 500

Ca. 1000

Ca. 2000

Ca. 3000

Base value(KOH mg/g)

224 ± 20

110 ± 10

56 ± 5

Drying time2

ASTM D5895 -03

hours

<2

<2

Paint3

Hardness(Persoz)

ISO 1522

46

59

Glossiness

ISO 2813

%

99

97

Chemical resistance

ISO 4211

4

4

Heat resistance: 120 Heated in the oven for 50 days

1. Solid content % w/w = 38, prepolymer NCO/OH ratio = 1.5, Preparation by acetone method
2. Completely dry (23℃, 50% RH)
3. Measured on a stainless steel plate after 7 days at a temperature of 23°C and a relative humidity of 50% (ISO 1514)

Water resistance: submerged at 8060 days in the water
Oil resistance: 100℃
Immersion in BP CS 150 for 30 days
Weather resistance: 200 hours of exposure using a 340 nm wavelength beam through a weathering instrument
Radiation amount 35 Wm2/nm
Black mark temperature 65
± 3
Relative humidity
​ ​ ​ ​ Dry for 102 minutes, then immediately spray with water for 18 minutes
(Rain test)

an>immersed in BP CS 150 for 30 days
Weather resistance: 200 hours of exposure using a 340 nm wavelength beam through a weathering instrument
Radiation amount 35 Wm2/nm
Black mark temperature 65
± 3
Relative humidity
​ ​ ​ ​ Dry for 102 minutes, then immediately spray with water for 18 minutes
(Rain test)