Covestro Bayhydur 401-60 PGDA water-based PU curing agent weather and chemical resistance

Product Features
A hydrophilic modified aliphatic polyisocyanate based on isophorone diisocyanate (IPDI), Bayhydur® 401-60 PGDA can be used as a co-reactant in water-based resins and in the preparation of resistant Curing agents for chemical and weather-resistant coatings

Form of Supply
About 60% propylene glycol diethyl ester solution

Feature data*

Features

Value

Measurement units

Method

NCOContent

about8.5

%

M105-ISO 11909

Viscosityat23°C

about1100

mPa·s

M014-ISO 3219/A.3

Color value(Hazen)

≤60

M017-EN 1557

IPDIMonomer content

<0.30

%

M106-ISO 10283

*This data is for reference only. The product specifications that should be followed are subject to the final released information.

Other data**

Features

Value

Measurement units

Method

Equivalent

about494

Flashpoint

about84

°C

DIN EN ISO 2719

Densityat20°C

About1.11

g/cm3

DIN 51757

**This data is general information.

Solubility/Dilution
Generally speaking, Bayhydur® 401-60 PGDA can be diluted with a variety of polar to non-polar aliphatic solvents and is commonly used in formulated paints. Can be diluted with polar solvents to 20% solid content. The storage stability of the diluent must be thoroughly tested, especially when using gasoline-based diluents and this needs to be done with care and skill. It is recommended to add Bayhydur® 401-60 PGDA to gasoline-soluble adhesives. Only use polyurethane grade solvents (less than 0.05% water content). The solvent cannot contain reactive groups such as hydroxyl or amino groups.

Compatibility
Generally speaking, Bayhydur® 401-60 PGDA can be mixed with various Desmodur® and Bayhydur® types, such as Desmodur® N3300 or N3600, Bayhydur® 3100, XP 2655 or XP 2547.
​ ​ However, compatibility must be tested in every case. At the same time, Bayhydur® 401-60 PGDA can be dispersed in various water-based adhesives such as bayhydrol® types, such as Bayhydrol® A2470, A2646, A242, A2845 and U2755.
The overall formulation (solids content, co-solvent content, type of co-solvent) needs to be considered to achieve a stable and appropriate working formulation.
​ ​ ​ If you require technical support, please ask your supplier.

Features/Applications
Bayhydur® 401-60 PGDA is easily emulsified in the water phase to form water-based paint or adhesive, and is mainly used as a co-crosslinking agent for Bayhydrol® arranged water-based resins.
By adding Bayhydur® 401-60 PGDA to the HDI-based Bayhydur crosslinker, the coating properties of two-component polyurethane coatings such as Bayhydur®
A typical mixture of Bayhydur® 401-60 PGDA and the HDI-based Bayhydur crosslinkers described above contains 5-30% Bayhydur® 401-60 PGDA in the total solids of the crosslinker.
The advantages of Bayhydur® 401-60 PGDA are as follows:
Final performance, such as
• Increased surface hardness;
• Increased chemical resistance and solvent resistance.
Application performance, such as
• Significantly longer pot life, even at high processing temperatures;
• Dry faster;
• Improved robustness, including increased bubble-free layer thickness.

/span>

About1.11

g/cm3

DIN 51757

**This data is general information.

Solubility/Dilution
Generally speaking, Bayhydur® 401-60 PGDA can be diluted with a variety of polar to non-polar aliphatic solvents and is commonly used in formulated paints. Can be diluted with polar solvents to 20% solid content. The storage stability of the diluent must be thoroughly tested, especially when using gasoline-based diluents and this needs to be done with care and skill. It is recommended to add Bayhydur® 401-60 PGDA to gasoline-soluble adhesives. Only use polyurethane grade solvents (less than 0.05% water content). The solvent cannot contain reactive groups such as hydroxyl or amino groups.

Compatibility
Generally speaking, Bayhydur® 401-60 PGDA can be mixed with various Desmodur® and Bayhydur® types, such as Desmodur® N3300 or N3600, Bayhydur® 3100, XP 2655 or XP 2547.
​ ​ However, compatibility must be tested in every case. At the same time, Bayhydur® 401-60 PGDA can be dispersed in various water-based adhesives such as bayhydrol® types, such as Bayhydrol® A2470, A2646, A242, A2845 and U2755.
The overall formulation (solids content, co-solvent content, type of co-solvent) needs to be considered to achieve a stable and appropriate working formulation.
​ ​ ​ If you require technical support, please ask your supplier.

Features/Applications
Bayhydur® 401-60 PGDA is easily emulsified in the water phase to form water-based paint or adhesive, and is mainly used as a co-crosslinking agent for Bayhydrol® arranged water-based resins.
By adding Bayhydur® 401-60 PGDA to the HDI-based Bayhydur crosslinker, the coating properties of two-component polyurethane coatings such as Bayhydur®
A typical mixture of Bayhydur® 401-60 PGDA and the HDI-based Bayhydur crosslinkers described above contains 5-30% Bayhydur® 401-60 PGDA in the total solids of the crosslinker.
The advantages of Bayhydur® 401-60 PGDA are as follows:
Final performance, such as
• Increased surface hardness;
• Increased chemical resistance and solvent resistance.
Application performance, such as
• Significantly longer pot life, even at high processing temperatures;
• Dry faster;
• Improved robustness, including increased bubble-free layer thickness.